Flexible Cables

Wires & Cables

A cable consists of two main parts: The Conductor and the Insulation.

CONDUCTOR:

Conductors for Cables are drawn from electrolytic grade Copper / Aluminium to ensure compliance with global standards . Annealed conductors are bunched together on custom built heavy duty bunching machines to impart concrete shape to the conductor.


INSULATION:

Solid & Bunched conductors are insulated on ultra modern extrusion machines with high technology P.V.C. Compound, which ensures extra flexibility, ideally suited for conduit & concealed wiring. To manufacture multicore cables, the insulated cores are laid up to form a concentric shape. Inner cores are coded for identification as per National / International coding system or as per customer’s specifications.

Outer sheathing is also provided with special soft PVC compound to minimize chances of electrical failures which may cause damage to expensive appliances, instruments & machinery etc.


QUALITY CONTROL:

Quality standards are in-built into every “Capital Cables” product Rigid tests and checks at every step, from raw material through manufacturing stages and finally up to the finished product ensure that “Capital Cables” products meet with international standards and therefore, consumer approval.

FLEXIBLE CABLES TECHNICAL DATA:

“Capital Cables” PVC insulated flexible single core, manufactured with bright annealed bare copper conductor for flexible use, insulated with Di- Electric grade PVC Compound. Impervious to oil, water, petrol, acids and greases generally for working voltage up to and included 1100 Volts.


CONDUCTOR

INSULATION

AREA

NO.  & SIZE OF WIRE

DIAMETER
OF WIRE

MAX.
RESISTANCE
AT 20°C

DC OR SINGLE
PHASE AC
SEPARATE
IN AIR

NOMINAL
THICKNESS

NOMINAL
OVERALL
DIAMETER

SQ.   MM.  MM

MM

OHM/KM.

AMPS.

MM

MM

0.50

16/.2O

0.95

37.50

4

0.6

2.30

0.75

24/.20

1.24

25.00

6

0.6

2.55

1.00

32/.20

1.31

18.70

10

0.6

2.70

1.50

48/.20

1.64

13.00

15

0.6

2.95

2.50

80/.20

2.08

7.98

20

0.7

3.65

4.00

128/.20

2.64

4.95

25

0.8

4.35

6.00

85/. 30

3.2

3.124

46

0.8

5.65

10.0

140/. 30

4.6

1.88

64

1.0

7.15

16.0

101/.45

5.9

1.140

85

1.4

8.95

25.0

168/.45

7.6

0.721

112

1.4

10.65

35.0

220/.45

8.7

0.525

138

1.4

11.75

50.0

325A45

10.6

0.362

172

1.6

14.05

70.0

440/.45

12.3

0.261

214

1.8

16.15

95.0

485/. 50

14.7

0.195

254

1.9

18.75

120.0

614/. 50

16.7

0.152

300

2.1

21.25

150.0

943A45

18.3

0.125

340

2.2

22.50

185.0

925/.50

20.3

0.101

390

2.5

25.50

240.0

1221/.50

23.0

0.076

460

2.5

28.50

CONDUCTOR

INSULATION

CROSS
SECTIONAL

NO. & SIZE
OF WIRE

COPPER C.R.
AT 20°C

ALUMINIUM
CAPACITY
COPPER

CURRENT
CARRYING
THICKNESS

NOMINAL
THICKNESS OF
INSULATION

NOMINAL
OVERALL
DIAMETER

CU

AL

SQ. MM.

MM.

OHM / KM.

OHM/KM.

AMPS.

AMPS.

MM.

MM.

1.0

1/1.12

17.70

18

0.7

2.55

1.5

1/1.38

11.90

19.7

25

20

0.7

2.80

2.5

1/1.78

7.14

11.8

32

25

0.8

3.40

4.0

1/2.24

4.47

7.39

45

35

0.8

3.85

6.0

1/2.76

2.97

4.91

55

45

0.8

4.40

10.0

1/3.57

1.77

2.94

75

60

1.0

5.60

16.0

7/1.70

1.12

1.89

95

75

1.0

7.10

25.0

7/2.14

0.710

1.17

125

100

1.2

885

30.0

7/2.52

0.520

0.861

150

120

1.2

9.90

50.0

19/1.78

0.360

0.595

190

150

1.4

11.90

70.0

19/2.14

0.265

0.373

240

185

1.4

13.50

95.0

19/2.52

0.190

0.250

280

215

1.6

15.70

120.0

37/2.03

0.151

0.211

300

240

1.6

17.40

150.0

37/2.24

0.121

0.195

350

270

1.8

19.30

CONDUCTOR

INSULATION

SHEATH

OVERALL DIAMETER

AREA

NO. & SIZE OF WIRE

DIAMETER

RESISTANCE
AT 20°C

CURRENT
CARRYING
CAPACITY

THICKNESS
NOMINAL

THICKNESS
NOMINAL

2 CORE

NOMINAL
3 CORE

4 CORE

SQ. MM

MM

MM

OHM/KM.

AMPS.

MM

MM

MM

MM

MM

0.50

16/.20

0.95

39.00

3

0.6

0.9

6.50

6.85

7.45

0.75

24/.20

1.24

26.00

6

0.6

0.9

7.00

7.40

8.05

1.00

32/.20

1.31

19.50

10

0.6

0.9

7.30

7.75

8.45

1.50

48/.20

1.64

13.00

15

0.6

0.9

7.80

8.25

9.25

2.50

80/.20

2.08

7.98

20

0.7

1.0

9.40

10.00

10.95

4.00

128/.20

2.64

4.95

25

0.8

1.0

10.75

11.50

12.65

CONDUCTOR

INSULATION

SHEATH

OVERALL DIAMETER

AREA

NO. & SIZE OF WIRE

DIAMETER

RESISTANCE
AT 20°C

CURRENT
CARRYING
CAPACITY

THICKNESS
NOMINAL

THICKNESS
NOMINAL

2 CORE

NOMINAL
3 CORE

4 CORE

SQ. MM

MM

MM

OHM/KM.

AMPS.

MM

MM

MM

MM

MM

0.50

16/.20

0.95

39.00

3

0.6

0.9

6.50

6.85

7.45

0.75

24/.20

1.24

26.00

6

0.6

0.9

7.00

7.40

8.05

1.00

32/.20

1.31

19.50

10

0.6

0.9

7.30

7.75

8.45

1.50

48/.20

1.64

13.00

15

0.6

0.9

7.80

8.25

9.25

2.50

80/.20

2.08

7.98

20

0.7

1.0

9.40

10.00

10.95

4.00

128/.20

2.64

4.95

25

0.8

1.0

10.75

11.50

12.65